INEOS PP N02J-00
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | INEOS Olefins & Polymers USA |
| Trademark: | INEOS PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1cSGpp_INEOS-PP-N02J-00.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| N02J-00 is a low melt flow rate, high impact copolymer polypropylene for sheet extrusion and thick wall injection molding applications. It offers a superior balance of stiffness and impact strength for thermoformed articles where freezer to microwave performance is required. Typical applications include appliances, compounding, consumer products, housewares, and rigid packaging. Benefits include enhanced room temperature and low temperature impact and enhanced stiffness. This material meets the requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 90 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 28.9 | MPa | |
| Break | 17.1 | MPa | |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield | 5.4 | % | |
| Break | 160 | % | |
| Flexural Modulus - 1% Secant | 1580 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 75 | J/m | |
| 23°C | 680 | J/m | |
| Notched Izod Impact (Area) | ASTM D256 | ||
| -20°C | 7.10 | kJ/m² | |
| 23°C | 67.5 | kJ/m² | |
| Instrumented Impact, Ductility | ASTM D3763 | ||
| -20°C | Ductile | ||
| 23°C | Ductile |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 116 | °C | |
| 1.8 MPa, Unannealed | 61.1 | °C | |
| Vicat Softening Temperature | 153 | °C | ASTM D1525 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss (60°) | 59 | ASTM D2457 |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecnoprene® F60K5 UA NAT005 | SO.F.TER. SPA | PP Homopolymer | Tecnoprene® |
| VENELENE® 8504UV8D | Poliolefinas Internacionales, C.A. (Polinter) | MDPE | VENELENE® |
| WEVO-CHEMIE Polyurethanes PU 930 M/600 | WEVO-CHEMIE GmbH | PUR, Unspecified | WEVO-CHEMIE Polyurethanes |
| Geon™ Vinyl Flexible R100AE | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| DOW™ HDPE DMDD-1210 NT 7 | The Dow Chemical Company | HDPE | 陶氏高密度聚乙烯 |