AKROMID® A3 GF 30 4 L black (4678)
| Category: | Nylon 66+PP , Polyamide 66 + PP |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1cOClw_AKROMID-A3-GF-30-4-L-black-4678-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® A3 GF 30 4 L black (4678) is a 30% glass fibre reinforced and hydrolysis-/ chemical stabilised polyamide-blend with a reduced density compared to standard PA6.6 GF 30 Applications are mainly functional parts in the heating- and cooling system in the automotive industry, where a weight and cost reduction is required |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.26 | -- | g/cm³ | ISO 1183 |
| Humidity Absorption - 62% RH (70°C) | 1.2 | -- | % | ISO 1110 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Reinforcement Content | 30 | -- | % | ISO 1172 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 8600 | 7000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 150 | 110 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.8 | 4.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 8600 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 220 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 16 | 16 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 70 | 66 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 246 | -- | °C | ISO 75-2/A |
| Melting Temperature 3 | 262 | -- | °C | DIN EN 11357-1 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 4(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10 K/min, DSC |
| 4 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polylink Polymer P-11030-GF | Polylink Polymers (India) Ltd. | TPO | Polylink Polymer |
| Sindustris ABS LLG850W | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| Triapol® Blends C3 K46 PRTA011 BS310 MSP | Petropol Industry and Trade of Polymers LTDA | PC+ABS | Triapol® Blends |
| TRIREX® Compound 3025G10 | Samyang Corporation | PC | TRIREX® Compound |
| DIOSHY® TPEE E955D-GS | DIOSHY Co.,Ltd. | TPEE | DIOSHY® |