Sekisui PVC HA-05H
| Category: | PVC, Unspecified , Polyvinyl Chloride |
| Manufacturer: | Sekisui (Hong Kong) Limited |
| Trademark: | Sekisui PVC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1bN8yk_Sekisui-PVC-HA-05H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Sekisui PVC HA-05H is a polyvinyl chloride product,. It is available in the Asia-Pacific region. The main characteristics are: high liquidity. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.54 | g/cm³ | JIS K7112 |
| Apparent Density | 0.50 - 0.60 | g/cm³ | JIS K6720-2 |
| K-Value | 52.0 | JIS K6720-2 | |
| Chlorine Content | 65.0 | wt% | ISO 1158 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Loss | wt% | JIS K6720-2 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Temperature - Flex | 87 | °C | JIS K6745 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 57.0 | MPa | JIS K7113 |
| Tensile Strain (Break) | 50 | % | JIS K7113 |
| Flexural Modulus | 2750 | MPa | JIS K7171 |
| Flexural Stress | 86.0 | MPa | JIS K7171 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 15 | kJ/m² | JIS K7111 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 96.0 | °C | JIS K7207 |
| 1.8 MPa, not annealed | 86.0 | °C | JIS K7191-1 |
| Vicat Softening Temperature | 103 | °C | JIS K7206 |
| CLTE - Flow | 7.0E-5 - 7.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | |
|---|---|---|---|
| Volume Resistivity 1(23°C) | 1.0E+15 | ohms·cm | |
| Dielectric Strength 2 | 47 - 63 | kV/mm | |
| Dielectric Constant | |||
| 60 Hz | 3.08 | ||
| 1 MHz | 3.20 - 3.60 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flow Rate (Flow Tester): 0.12 ml.sec |
| Note Message | |
|---|---|
| 1 . | 50% RH |
| 2 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL TP-GFMF1 | Polymer Resources Ltd. | PBT | PRL |
| TRANSMARE® BIO 18LANF20-0.001 | Transmare Compounding B.V. | PLA | TRANSMARE® BIO |
| Axiall PVC 4441 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Clariant Nylon 6/6 66G13-L | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Elvax® 3165 | DuPont Packaging & Industrial Polymers | EVA | Elvax® |