LNP™ VERTON™ RV007ESS compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ VERTON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1b5TlQ_LNP-VERTON-RV007ESS-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP VERTON* RF-7007 EM HS is a compound based on Nylon 66 resin containing Long Glass. Added features of this material include: Easy Molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792, ISO 1183 |
| Water Absorption (24 hr, 50% RH) | 0.97 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 12000 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 205 | MPa | ASTM D638 |
| Break | 214 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.1 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 9880 | MPa | ASTM D790 |
| -- | 10200 | MPa | ISO 178 |
| Flexural Stress | 309 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 280 | J/m | ASTM D256 |
| -40°C 1 | 25 | kJ/m² | ISO 180/1A |
| 23°C 2 | 29 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 245 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 3 | 252 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 282 to 293 | °C | |
| Middle Temperature | 288 to 299 | °C | |
| Front Temperature | 288 to 299 | °C | |
| Processing (Melt) Temp | 288 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 80*10*4 |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUSTASON PSU | Röchling Sustaplast SE & Co. KG | PSU | SUSTASON |
| Boltaron 4335 | Boltaron Performance Products | PMMA+PVC | Boltaron |
| Dugdale PVC Flexible Injection Molding - Shore A 58 Compound | Dugdale Plc | PVC, Flexible | Dugdale PVC |
| Lion Idemitsu Composites PPS C-7075SG | Lion Idemitsu Composites Co., Ltd. | PPS | Lion Idemitsu Composites PPS |
| ULTEM™ 2300R resin | SABIC Innovative Plastics | PEI | ULTEM™ |