TRANSMARE® 22CT40-0.001
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Transmare Compounding B.V. |
| Trademark: | TRANSMARE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1YVe3W_TRANSMARE-22CT40-0-001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRANSMARE® 22CT40-0.001 is a 40% fine white talc filled polypropylene copolymer. This grade contains a mould release agent. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 17 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 69 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (4.00 mm) | 3500 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 4.00 mm | 26.0 | MPa | |
| Break, 4.00 mm | 24.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 4.00 mm | 1.9 | % | |
| Break, 4.00 mm | 3.5 | % | |
| Flexural Modulus | 4210 | MPa | ISO 178 |
| Flexural Stress | 46.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1A | ||
| -40°C | 1.2 | kJ/m² | |
| 23°C | 2.4 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1U | ||
| -40°C | 14 | kJ/m² | |
| 23°C | 22 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C | 1.7 | kJ/m² | |
| 23°C | 3.0 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -40°C | 13 | kJ/m² | |
| 23°C | 18 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 129 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 67.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 154 | °C | ISO 306/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Moisture | < 0.20 | % | |
| Rear Temperature | 170 | °C | |
| Middle Temperature | 230 | °C | |
| Front Temperature | 240 | °C | |
| Nozzle Temperature | 250 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Injection Rate | Moderate-Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SRP3606A | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Eco-Solutions GP9002W | MINIMA Technoloy Co. Ltd. | Biodeg Polymers | Eco-Solutions |
| Karina BLACK PVC COMPOUND 813-48/ 1-A-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lumiplas® LD7890 | LG Chem Ltd. | PC | Lumiplas® |
| OnFlex™ S HF 60A-3S1982 | PolyOne Corporation | TPE | OnFlex™ |