InnoPlus HD2308J
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | PTT Global Chemical Public Company Limited |
| Trademark: | InnoPlus |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1YFKQ4_InnoPlus-HD2308J.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
InnoPlus HD2208J and HD2308J are high density polyethylene injection molding grade. They are tailored with narrow molecular weight distribution (MWD) result for good impact strength. Furthermore, they are UV stabilizer added that give the excellent UV resistance for outdoor applications such as auto part and industrial product. Typical Application: Crates, Pallets, Garbage bins, Industrial tubes, Fruit baskets, Caps and Closures |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.962 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (25% Igepal, F50) | 5.00 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 65 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 29.4 | MPa | |
| Break | 11.8 | MPa | |
| Tensile Elongation (Break) | 750 | % | ASTM D638 |
| Apparent Bending Modulus | 1080 | MPa | ASTM D747 |
| Flexural Modulus | 1470 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 1 | 39 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 125 | °C | ASTM D1525 2 |
| Peak Melting Temperature | 131 | °C | ASTM D3418 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 170 to 200 | °C | |
| Middle Temperature | 170 to 200 | °C | |
| Front Temperature | 170 to 200 | °C | |
| Nozzle Temperature | 185 to 205 | °C |
| Note Message | |
|---|---|
| 1 . | Complete break |
| 2 . | Rate A (50°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shuang-Bang WM-8207N | Shuang-Bang Industrial Corp. | Film, TPU | Shuang-Bang |
| TECHNYL® A R 218 V25 BLACK | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| CEFOR™ 1221P | The Dow Chemical Company | LLDPE | CEFOR™ |
| Elastollan® 685 A | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |
| Electrafil® PA6/6 05002 | Techmer Engineered Solutions | Nylon 66 | Electrafil® |