Eporex® HIPS 825
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Eternal Plastics Co., Ltd. |
| Trademark: | Eporex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1XgvRu_Eporex-HIPS-825.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Eporex® HIPS 825 is a High Impact Polystyrene material. It is available in North America for injection molding. Important attributes of Eporex® HIPS 825 are:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 6.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 64 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 25.5 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 50 | % | ASTM D638 |
| Flexural Modulus | 2000 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 39.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 80.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 97.8 | °C | ASTM D1525 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TYNAB® GM70 | Tyne Plastics LLC. | ABS | TYNAB® |
| Elastron® D D100.A75.N | Elastron USA, Inc. | SBS | Elastron® D |
| EMAREX® 400 GF13 | MRC Polymers, Inc. | Nylon 66 | EMAREX® |
| HI-ZEX™ 530B | Prime Polymer Co., Ltd. | HDPE | HI-ZEX™ |
| Plaslube® PA6/6 GF30 TS15 | Techmer Engineered Solutions | Nylon 66 | Plaslube® |