RTP 1800 A UV
| Category: | PC+Acrylic , Polycarbonate + Acrylic (PMMA) |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1XHhfb_RTP-1800-A-UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Additive |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.40 - 0.80 | % | ASTM D955 |
| Water Absorption (Saturation) | 0.26 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 45 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2410 | MPa | ASTM D638 |
| Tensile Strength | 61.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 60 | % | ASTM D638 |
| Flexural Modulus | 2070 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 3.18 mm | 210 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 1600 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 123 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 101 | °C | ASTM D648 |
| CLTE - Flow | 9.4E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dielectric Constant (1 MHz) | 2.72 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 9.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Additional Information |
|---|
| The value listed as UL 94, was tested in accordance with RTP Company Testing. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 218 - 260 | °C | |
| Middle Temperature | 218 - 260 | °C | |
| Front Temperature | 218 - 260 | °C | |
| Injection Pressure | 55.2 - 68.9 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Durethan® BKV 55 TPX 900116 | LANXESS GmbH | Nylon 6 | Durethan® |
| Geon™ Vinyl Flexible 86479 Tran | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Hostalen GM 5010 T3 black | LyondellBasell Industries | HDPE | Hostalen |
| POLYFORT® FPP 1068 | A. Schulman Inc. | PP, Unspecified | POLYFORT® |
| TOPAS® 6017S-04 | Topas Advanced Polymers, Inc. | COC | TOPAS® |