RTP 2099 X 121241 B
| Category: | PLA+PC , Polylactic Acid + PC |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1WDwhi_RTP-2099-X-121241-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC-PLA Blend - ESD Protection - Permanently Anti-static - 26% Renewable Resource Content |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.60 | % | ASTM D955 |
| Moisture Content | 0.020 | % |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Static Decay 1 | sec | FTMS 101C 4046.1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1720 | MPa | ASTM D638 |
| Tensile Strength | 35.9 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 7.0 | % | ASTM D638 |
| Flexural Modulus | 1720 | MPa | ASTM D790 |
| Flexural Strength | 55.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 850 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 85.0 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+10 - 1.0E+12 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+8 - 1.0E+11 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, ** Values per RTP Company testing.) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 4.0 | hr | |
| Dew Point | -40.0 | °C | |
| Processing (Melt) Temp | 221 - 243 | °C | |
| Mold Temperature | 23.9 - 71.1 | °C | |
| Injection Pressure | 55.2 - 103 | MPa |
| Injection instructions |
|---|
| Desiccant Type Dryer Required. |
| Note Message | |
|---|---|
| 1 . | MIL-PRF-81705D, 5kV to 50 V, 12% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULATEC® PP EC 1009 HI BLACK | A. Schulman Europe | PP Copolymer | SCHULATEC® |
| Multiuse Leostomer® LJ-3160N | Riken Technos Corp. | TPU, Unspecified | Multiuse Leostomer® |
| Fainplast PVC PK 88/2-UV | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Latiohm 80-04 PD01 G/30 | LATI S.p.A. | PPS | Latiohm |
| TechnoFin PP LR 23 | TechnoCompound GmbH | PP, Unspecified | TechnoFin |