Infino WP-1053
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1W9LMB_InfinoWP1053.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino WP-1053 is a polycarbonate acrylonitrile butadiene styrene (PC ABS) product,. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: automotive industry. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.12 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/10.0 kg) | 45 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 112 | ASTM D785 | |
| R scale | 112 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2200 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 1 | 53.0 | MPa | ASTM D638 |
| Yield | 54.0 | MPa | ISO 527-2/50 |
| Fracture | 46.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 78 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 2 | 2200 | MPa | ASTM D790 |
| -- 3 | 2250 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 4 | 74.0 | MPa | ASTM D790 |
| -- 5 | 75.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 6(23°C) | 45 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 470 | J/m | ASTM D256 |
| 23°C 7 | 45 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, unannealed, 4.00mm | 115 | °C | ISO 75-2/B |
| 0.45 MPa, annealing, 4.00mm | 119 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 6.40mm | 105 | °C | ASTM D648 |
| 1.8 MPa, not annealed, 4.00mm | 94.0 | °C | ISO 75-2/A |
| 1.8 MPa, annealing, 4.00mm | 106 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 113 | °C | ISO 306/B50 |
| -- | 116 | °C | ISO 306/B120 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 2.8 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | Thickness: 4mm |
| 7 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultrason® E 6020 P | BASF Corporation | PESU | Ultrason® E |
| APEX® 1700-85 | Teknor Apex Company | PVC, Flexible | APEX® |
| Grivory® HTV-3H1 nat | EMS-GRIVORY | Nylon 6I/6T | Grivory® |
| LNP™ THERMOTUF™ W1000I compound | SABIC Innovative Plastics Europe | PBT | LNP™ THERMOTUF™ |
| Sylvin 8203-55 Green 3172 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |