Vipel® F701-FBN-15
| Category: | Polyester Alloy , Polyester Alloy |
| Manufacturer: | AOC, L.L.C. |
| Trademark: | Vipel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1SiCeh_VipelF701FBN15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AOC's Vipel F701 Series resins are high molecular weight, two-stage isophthalic, unsaturated polyester resin with the wet out, cure and handling characteristics of general purpose resins. They have an excellent shelf life and are ideal for filament winding and spray-up. A few selected resins are listed below including the high viscosity base resin, Vipel F701-FHG-00. BENEFITS Corrosion resistance AOC's Vipel F701 series resins provide excellent corrosion resistance when used in contact with inorganic and organic acids. Solvent resistance is field-proven for many petroleum products such as kerosene, heating oil and crude oils. Refer to AOC's "Corrosion Resistant Resin Guide" for corrosion resistance information or for questions regarding suitability of a resin to any particular chemical environment contact AOC. Versatile Suitable for various fabricating methods such as hand lay-up, spray-up and filament winding. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Styrene Content | 48 | % |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Gel to Peak | 10.0 | min | |
| Peak Exotherm | 199 | °C | |
| Thixotropic Index 1 | 2.50 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Barcol Hardness | 43 | ASTM D2583 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3790 | MPa | ASTM D638 |
| Tensile Strength | 83.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.8 | % | ASTM D638 |
| Flexural Modulus | 4210 | MPa | ASTM D790 |
| Flexural Strength | 127 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 107 | °C | ASTM D648 |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Density | 1.06 | g/cm³ | |
| Viscosity (Brookfield LV) | 0.55 | Pa·s | |
| Gel Time (25°C) | 15 | min |
| Note Message | |
|---|---|
| 1 . | 2/20 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PBT TE5007F | Sincerity Australia Pty Ltd. | PC+PBT | Sindustris PBT |
| EVALENE® HDPE HB33531 | JG Summit Petrochemical Corporation | HDPE | EVALENE® HDPE |
| INEOS Wire & Cable BPD2142 | INEOS Olefins & Polymers Europe | LDPE | INEOS Wire & Cable |
| Hostacom HYP 376D 201104 | LyondellBasell Industries | PP Homopolymer | Hostacom |
| Sylvin 8203-55 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |