Daplen™ EE209AE
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Borealis AG |
| Trademark: | Daplen™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1SRh5A_Daplen-EE209AE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Daplen EE209AE is a 20% mineral filled elastomer modified polypropylene compound intended for injection moulding. This material has excellent balanced mechanical properties, gives a good surface quality and is easy to process. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 13 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| -- 1 | 0.50 | % | Internal method |
| 90°C, 2 hours | 0.10 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 132/10) | 26.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1400 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 16.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 6.0 | % | ISO 527-2/50 |
| Fracture | 200 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 1500 | MPa | ISO 178 |
| Flexural Stress | 16.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 4.0 | kJ/m² | ISO 179/1eA |
| -20°C | 20 | kJ/m² | ISO 179/1eA |
| 23°C | 65 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU | |
| Notched Izod Impact | ISO 180/1A | ||
| -20°C | 27 | kJ/m² | ISO 180/1A |
| 23°C | 52 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 93.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 52.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 115 | °C | ISO 306/A50 |
| -- | 37.0 | °C | ISO 306/B50 |
| CLTE - Flow (-30 to 80°C) | 4.3E-5 | cm/cm/°C | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Hopper Temperature | 40.0 - 80.0 | °C | |
| Processing (Melt) Temp | 220 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Holding Pressure | 30.0 - 60.0 | MPa |
| Injection instructions |
|---|
| Back pressure: Low to mediumScrew speed: Low to mediumFlow front speed: 100 - 200 mm/s |
| Note Message | |
|---|---|
| 1 . | disk |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SOLARENE S334 | Dongbu Hannong Chemical | PS (GPPS) | SOLARENE |
| Epolene® C-16P | Westlake Chemical Corporation | LDPE | Epolene® |
| Estane® 2103-90AEL TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyether | Estane® |
| Orgalloy® LE 60LM | Arkema | Nylon 6 Alloy | Orgalloy® |
| SABIC® LLDPE RG50035 | Saudi Basic Industries Corporation (SABIC) | LLDPE | SABIC® LLDPE |