Generic PPE+PS+Nylon
| Category: | PPE+PS+Nylon , Polyphenylene Ether + PS + Nylon |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1SGKfD_Generic-PPE-PS-Nylon.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PPE+PS+Nylon This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.07 - 1.12 | g/cm³ | ASTM D792 |
| 23°C | 1.07 - 1.25 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 8.0 - 21 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 7.50 - 19.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 23°C | 1.2 - 1.8 | % | ASTM D955 |
| Transverse flow : 23°C | 1.1 - 1.3 | % | ASTM D955 |
| Water Absorption | |||
| 23°C, 24 hr | 0.39 - 0.60 | % | ASTM D570 |
| Saturated, 23°C | 3.5 - 4.2 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.2 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 75.0 - 90.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 1820 - 3320 | MPa | ASTM D638 |
| 23°C | 2000 - 3050 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 53.5 - 65.6 | MPa | ASTM D638 |
| Yield, 23°C | 50.0 - 65.2 | MPa | ISO 527-2 |
| Fracture, 23°C | 49.8 - 60.2 | MPa | ASTM D638 |
| Fracture, 23°C | 45.0 - 55.5 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield, 23°C | 4.7 - 5.0 | % | ASTM D638 |
| Yield, 23°C | 3.5 - 5.1 | % | ISO 527-2 |
| Fracture, 23°C | 2.2 - 100 | % | ASTM D638 |
| Fracture, 23°C | 2.8 - 51 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 1840 - 2730 | MPa | ASTM D790 |
| 23°C | 1860 - 2850 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 73.5 - 85.7 | MPa | ASTM D790 |
| 23°C | 70.0 - 103 | MPa | ISO 178 |
| Yield, 23°C | 74.7 - 99.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 11 - 55 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 73 - 680 | J/m | ASTM D256 |
| 23°C | 9.5 - 55 | kJ/m² | ISO 180 |
| Instrumented Dart Impact (23°C) | 4.00 - 60.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 154 - 196 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 174 - 193 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 83.9 - 197 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 178 - 233 | °C | ASTM D1525 |
| -- | 169 - 246 | °C | ISO 306 |
| Linear thermal expansion coefficient | |||
| Flow | 7.5E-5 - 9.8E-5 | cm/cm/°C | ASTM E831 |
| Flow | 8.0E-5 - 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral | 5.9E-5 - 1.0E-4 | cm/cm/°C | ASTM E831 |
| Lateral | 8.9E-5 - 9.1E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity (23°C) | 0.23 - 0.24 | W/m/K | ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 4.0E+3 - 1.1E+15 | ohms·cm | ASTM D257 |
| Relative Permittivity (23°C) | 3.17 | IEC 60250 | |
| Dissipation Factor (23°C) | 0.024 - 0.072 | IEC 60250 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 99.7 - 110 | °C | |
| Drying Time | 2.5 - 3.5 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.069 - 0.070 | % | |
| Suggested Shot Size | 40 | % | |
| Hopper Temperature | 70.0 - 70.5 | °C | |
| Rear Temperature | 269 - 280 | °C | |
| Middle Temperature | 275 - 292 | °C | |
| Front Temperature | 279 - 306 | °C | |
| Nozzle Temperature | 281 - 295 | °C | |
| Processing (Melt) Temp | 282 - 305 | °C | |
| Mold Temperature | 78.1 - 100 | °C | |
| Back Pressure | 0.847 - 0.862 | MPa | |
| Screw Speed | 60 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PPE+PS+NylonThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL PEI-G30 | Polymer Resources Ltd. | PEI | PRL |
| Exxtral™ Performance Polyolefin BMU131 | ExxonMobil Chemical | TPO | Exxtral™ Performance Polyolefin |
| INNOPOL® PP CS 2-9522 T15SR | Inno-Comp Ltd. | PP Impact Copolymer | INNOPOL® PP |
| Sylvin 7833-75 Red 6260 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Rotuba CA MH | Rotuba Extruders, Inc. | CA | Rotuba CA |