LNP™ STAT-KON™ KS000MXL compound
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1PFnXS_LNP-STAT-KON-KS000MXL-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* STAT-KON* KS000MXL is a compound based on Acetal resin containing Stainless Steel. Added features of this grade include: Low Extractable, Metal Detectable. Also known as: LNP* STAT-KON* Compound KS000MXL Product reorder name: KS000MXL |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.73 | g/cm³ | |
| -- | 1.72 | g/cm³ | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 2.8 | % | |
| Across Flow : 24 hr | 2.5 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.13 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.21 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3010 | MPa | ASTM D638 |
| -- | 2880 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 52.0 | MPa | ASTM D638 |
| Yield | 52.0 | MPa | ISO 527-2/5 |
| Break 3 | 51.0 | MPa | ASTM D638 |
| Break | 51.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 11 | % | ASTM D638 |
| Yield | 11 | % | ISO 527-2/5 |
| Break 5 | 27 | % | ASTM D638 |
| Break | 26 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2680 | MPa | ASTM D790 |
| -- 7 | 2590 | MPa | ISO 178 |
| Flexural Stress | 75.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 58 | J/m | ASTM D256 |
| 23°C 8 | 6.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 930 | J/m | ASTM D4812 |
| 23°C 9 | 57 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 5.20 | J | ASTM D3763 |
| -- | 1.32 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 158 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 149 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 104 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 95.0 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 9.9E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 9.8E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.9E+12 | ohms | ASTM D257 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVALEN® PH 78 FRT 5 | Plastcom | PP, Unspecified | SLOVALEN® |
| Vinylbond 95-950-45 | Colorite Polymers | PVC, Flexible | Vinylbond |
| NuSil CV4-2500 | NuSil Technology | Silicone | NuSil |
| alphalon™ 27 D | Grupa Azoty ATT Polymers GmbH | Nylon 6 | alphalon™ |
| Petrotene® PP A3 T40 PRTA011 PH376 MSP | Petropol Industry and Trade of Polymers LTDA | PP Homopolymer | Petrotene® PP |