Badamid® B70 GF/M30 FR
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Bada AG |
| Trademark: | Badamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1Oyq1D_Badamid-B70-GF-M30-FR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Badamid®B70 GF/M30 FR is a polyamide 6 (nylon 6) material containing 30% glass \mineral. This product is available in Europe,. Badamid®The main characteristics of B70 GF/M30 FR are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.51 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 5.2 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.7 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 7800 | 5000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 130 | 95.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 2.0 | 4.0 | % | ISO 527-2/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 6.0 | 8.0 | kJ/m² | ISO 179/1eA |
| 23°C | 8.0 | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 45 | 55 | kJ/m² | ISO 179/1eU |
| 23°C | 50 | 65 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | |||
| -30°C | 5.0 | 6.0 | kJ/m² | ISO 180/1A |
| 23°C | 7.0 | 11 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 1 | ||||
| 0.45 MPa, not annealed | 215 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 200 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 222 | -- | °C | ISO 3146 |
| CLTE - Flow (4.00 mm) | 3.5E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Dielectric Constant (1 MHz) | 3.70 | 6.10 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.019 | 0.29 | IEC 60250 | |
| Comparative Tracking Index | 500 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | V-2 | -- | UL 94 |
| Additional Information |
|---|
| 干燥 Short-Term Heat Resistance, IEC 216, 20000 hrs: 190°CLong-Term Heat Resistance, IEC 216, 50% decrease of yield stress: 100°C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 260 - 280 | °C | |
| Mold Temperature | 80.0 - 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 110x10x4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VAMPAMID 66 0024 V0 | Vamp Tech | Nylon 66 | VAMPAMID |
| Ducor® 1101 P | Ducor Petrochemicals BV | PP Homopolymer | Ducor® |
| LNP™ STAT-KON™ ZX05043 compound | SABIC Innovative Plastics Europe | PPE+PS | LNP™ STAT-KON™ |
| PERLER® N0925000A10 | A.D. Compound S.p.A. | PP Copolymer | PERLER® |
| SD POLYCA™ IM5101V | Sumika Styron Polycarbonate Limited | PC | SD POLYCA™ |