Bergamid™ B70 G45 BK LS
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Bergamid™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1Nnugo_Bergamid-B70-G45-BK-LS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 6016133 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.52 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1(23°C, 4000 mm) | 0.080 to 0.60 | -- | % | ISO 294-4 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C, 4.00 mm, Injection Molded) | 13000 | 10000 | MPa | ISO 527-2/1 |
| Tensile Strength 2(23°C, 4.00 mm) | 192 | 150 | MPa | ISO 527 |
| Tensile Elongation 3(Break, 23°C, 4.00 mm) | 2.5 | 3.5 | % | ISO 527 |
| Flexural Modulus (23°C) | 12300 | -- | MPa | ISO 178 |
| Flexural Stress (23°C) | 290 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | 11 | -- | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C, Injection Molded) | 87 | -- | kJ/m² | ISO 179 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.800 to 3.00 mm, ALL) | HB | HB | Internal Method |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 240 to 280 | °C | |
| Mold Temperature | 65.0 to 85.0 | °C |
| Note Message | |
|---|---|
| 1 . | Bergmann method |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| BESTNYL SI00VI01BM | Triesa Plastics | Nylon 6 | BESTNYL |
| Celstran® TPU-CF40-01 | Celanese Corporation | TPU, Unspecified | Celstran® |
| CompaDur® 125 GF 20 black (045) | DimeLika Plast GmbH | PBT+PET | CompaDur® |
| EZPrene 9085A | ENPLAST Americas, a Ravago Group Company | TPV | EZPrene |
| Haysite Plastics H330 | Haysite Reinforced Plastics | Polyester, TS | Haysite Plastics |