VERSIFY™ 3401
| Category: | TPO (POE) , Elastomer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | VERSIFY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1NKSsZ_VERSIFY-3401.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VERSIFY™ 3401 Elastomer is a resin with a medium melt flow rate suitable for a wide variety of applications and fabrication processes, including cast film, extrusion and injection molding. It is an excellent resin for stretch films and soft films, and is an excellent choice for PP modification, giving consistent performance in hot and cold conditions. Main Characteristics
Applications
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.863 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Total Crystallinity | 14 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness 1 | ASTM D2240 | ||
| Shore A, Compression Molded | 72 | ||
| Shore D, Compression Molded | 22 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, Compression Molded) | 6.80 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, Compression Molded) | 600 | % | ASTM D638 |
| Flexural Modulus - 1% Secant (Compression Molded) | 22.7 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -29.8 | °C | Internal Method |
| Vicat Softening Temperature | < 20.0 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 55.0 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Gloss | ASTM D523 | ||
| 20°, 1000 µm, Compression Molded | 63 | ||
| 60°, 1000 µm, Compression Molded | 112 | ||
| Haze (2000 µm, Injection Molded) | 3.2 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Hardness after 10 seconds. |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vi-Chem PVC VNC80I | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Baoding 76E85 | Baoding Bangtai Polymeric New-Materials Co.,Ltd | TPU-Polyether | Baoding |
| BLUESTAR® PBT 403G-M20 | Nantong Zhonglan Engineering Plastics Co., Ltd. | PBT | BLUESTAR® |
| Karina BLUE COLOR CONCENTRATE 06/830-GE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| API II 645 | API II, Inc. | PS (HIPS) | API II |