LNP™ THERMOTUF™ OX96685 compound
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOTUF™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1MgG2g_LNPTHERMOTUFOX96685compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* THERMOTUF* OX96685 is a compound based on PPS resin containing proprietary fillers. Added feature of this grade is: Impact Modified. Also known as: LNP* THERMOTUF* Compound PDX-O-96685 Product reorder name: OX96685 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.48 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hours | 0.95 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.82 | % | ASTM D955 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.030 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.050 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6180 | MPa | ASTM D638 |
| -- | 6110 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture 2 | 94.0 | MPa | ASTM D638 |
| Fracture | 92.0 | MPa | ISO 527-2/5 |
| Tensile Strain | |||
| Yield | 2.6 | % | ISO 527-2/5 |
| Fracture 3 | 2.6 | % | ASTM D638 |
| Fracture | 2.7 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 4 | 5290 | MPa | ASTM D790 |
| -- 5 | 5360 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 133 | MPa | ISO 178 |
| Yield, 50.0mm span 6 | 134 | MPa | ASTM D790 |
| Fracture, 50.0mm span 7 | 131 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 110 | J/m | ASTM D256 |
| 23°C 8 | 11 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 550 | J/m | ASTM D4812 |
| 23°C 9 | 33 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 17.6 | J | ASTM D3763 |
| -- | 4.36 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 269 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 10 | 263 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 203 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 11 | 174 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ASTM D696 | ||
| Flow : -30 to 30°C | 4.2E-5 | cm/cm/°C | ASTM D696 |
| Lateral : -30 to 30°C | 6.9E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 304 - 316 | °C | |
| Middle Temperature | 321 - 332 | °C | |
| Front Temperature | 332 - 343 | °C | |
| Processing (Melt) Temp | 316 - 321 | °C | |
| Mold Temperature | 138 - 166 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2300.5 C | RTP Company | TPU-Polyester | RTP |
| EQUATE PE EMDA-6200 | EQUATE Petrochemical Company KSCC | HDPE Copolymer | EQUATE PE |
| Karina BLACK PVC COMPOUND -E 700-48/ 1 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 8600-85 Yellow 4173 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| HiFormer® Liquid Masterbatches | Clariant Corporation | TP, Unspecified | HiFormer® |