Hostacom HYS 2009R 105518
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1KTCef_HostacomHYS2009R105518.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hostacom HYS 2009R 105518 is an unfilled PP homopolymer, with high flowability, very high gloss, very good hot water resistance and high blooming resistance at elevated temperatures. Product is UL listed. The product is also available as a customized color matched, pellet form. This grade is delivered in 105518 color version. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.910 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 28 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 35.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1600 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 37.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 9.0 | % | ISO 527-2 |
| Flexural Modulus 1(23°C) | 1700 | MPa | ISO 178/A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.5 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 100 | °C | ISO 306/B |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Smoothblend® ABS-1100 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | ABS | Smoothblend® |
| TEREZ PA 6 7500 GF 30 AM | TER HELL PLASTIC GMBH | Nylon 6 | TEREZ PA 6 |
| TOTAL Polyethylene HDPE MS 201 BN | TOTAL Refining & Chemicals | HDPE | TOTAL Polyethylene |
| AKROMID® A3 S3 black (1043) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| Moplen HP525J | PolyMirae | PP Homopolymer | Moplen |