InnoTuf® TP-4055
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | InnoTuf® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1IqrwC_InnoTuf-TP-4055.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TP-4055 is an impact resistant polyurethane formulated for hand-batch processing, vacuum assist casting or meter mix dispense methods. Excellent physical properties can be obtained with a mild post cure without the utilization of mercury, MOCA, or TDI. TP-4055 is a tough polyethylene/polypropylene simulated product with a very low mixed viscosity. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Hardener | 1.07 | g/cm³ | |
| Cured | 1.08 | g/cm³ | |
| Base Resin | 1.21 | g/cm³ | |
| Molding Shrinkage - Flow | 0.10 to 0.50 | % | ASTM D2566 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 724 | MPa | ASTM D790 |
| Flexural Strength | 26.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 91 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 64.0 | °C | ASTM D648 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 100 Mix Ratio by Weight: 100 | ||
| Resin | Mix Ratio by Weight: 76 Mix Ratio by Volume: 67 | ||
| Demold Time | 120 to 240 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 38°C 1 | 0.075 | Pa·s | |
| 38°C 2 | 0.50 | Pa·s | |
| 38°C 3 | 1.6 | Pa·s | |
| Curing Time 4 | 26 | hr | |
| Gel Time | 6.0 to 10 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 65 to 75 | ASTM D2240 | |
| Tensile Strength | 31.8 | MPa | ASTM D638 |
| Tensile Elongation at Break | 35 | % | ASTM D638 |
| Note Message | |
|---|---|
| 1 . | Resin |
| 2 . | Mixed |
| 3 . | Hardener |
| 4 . | 2 hours at 150°F + 24 hours at 77°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SAXALAC™ 320U | SAX Polymers | ABS | SAXALAC™ |
| Sumikon® EME-6300HJ | Sumitomo Bakelite Co., Ltd. | Epoxy | Sumikon® |
| AKROMID® A3 GF 40 1 natural (2381) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| Geon™ Vinyl Rigid Extrusion 85857 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| Electrafil® PA6/6 03001 | Techmer Engineered Solutions | Nylon 66 | Electrafil® |