| Category: | PUR-Ester , Polyurethane (Polyester based) |
| Manufacturer: | Cook Composites and Polymers |
| Trademark: | Interpol |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1IQtv9_Interpol-47-5138-47-5205-20-Glass.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Interpol 47-5138/47-5205 20%Glass is a Polyurethane (Polyester based) (PUR-Ester) product filled with 20% glass fiber. It can be processed by casting or injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2410 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 3.7 | % | ASTM D638 |
| Flexural Modulus | 4310 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 145 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 450 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 140 | °C | ASTM D648 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 27 | ||
| Resin | Mix Ratio by Weight: 100 | ||
| Demold Time (100°C) | 960 | min |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 54.4 to 65.6 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom PP5133R B1 | Spartech Polycom | PP Homopolymer | Spartech |
| Bapolan® PS6445 | Bamberger Polymers, Inc. | PS (HIPS) | Bapolan® |
| KOPA® KN173MC | Kolon Plastics, Inc. | Nylon 6 | KOPA® |
| Huafon JF-W-3015C | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| OmniCarb™ PC CBFR0 HSV | OMNI Plastics, LLC | PC | OmniCarb™ |