STYRON™ 650 HF
| Category: | PS (GPPS) , General Purpose Polystyrene Resin |
| Manufacturer: | Trinseo |
| Trademark: | STYRON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1ICnrS_STYRON-650-HF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
STYRON™ 650 HF is a high melt flow rate general purpose resin specifically developed for medium to thick XPS board applications. It offers a unique balance of melt tension, processability and foaming behavior. Its high MFR also makes it very suitable for high dosing compounding applications. Main Characteristics
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 46 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield, 3.20 mm 1 | 4.90 | MPa | ASTM D638 |
| Yield, 3.20 mm | 4.90 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break, 3.20 mm 2 | 3.0 | % | ASTM D638 |
| Break, 3.20 mm | 3.0 | % | ISO 527-2/5 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 101 | °C | ISO 306/A120, ASTM D1525 3 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCLAIR® 8107 | NOVA Chemicals | LLDPE | SCLAIR® |
| NatureFlex™ 165NP | Innovia Films Ltd. | Cellulose, Regenerated | NatureFlex™ |
| HiFill FR® PA6/6 GF20 FR-NR | Techmer Engineered Solutions | Nylon 66 | HiFill FR® |
| LNP™ THERMOCOMP™ PF005S compound | SABIC Innovative Plastics | Nylon 6 | LNP™ THERMOCOMP™ |
| Sylvin 8260-75 Blue 8341 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |