TIPELIN® FS 471-02
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | MOL Petrochemicals Co. Ltd. |
| Trademark: | TIPELIN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1I305D_TIPELIN-FS-471-02.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TIPELIN FS 471-02 is a film grade of high density polyethylene copolymer (with hexene-1 as comonomer) grade. The product has high molecular mass, very good Tear strength and Dart drop resistance, low gel content, good vapour barrier properties. The grade contains antioxidant and acid scavenger. Applications TIPELIN FS 471-02 is recommended for extra thin packaging films, bags, shopping bags and garbage bags. TIPELIN FS 471-02 is suitable for food contact. The product complies with Food Contact Regulations. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.946 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.18 | g/10 min | |
| 190°C/21.6 kg | 15 | g/10 min | |
| 190°C/5.0 kg | 0.80 | g/10 min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 63 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 1200 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 25 µm, Blown Film | 25.0 | MPa | |
| TD : Yield, 25 µm, Blown Film | 23.0 | MPa | |
| MD : 25 µm, Blown Film | 53.0 | MPa | |
| TD : 25 µm, Blown Film | 47.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 25 µm, Blown Film | 700 | % | |
| TD : Break, 25 µm, Blown Film | 800 | % | |
| Dart Drop Impact (25 µm, Blown Film) | 95 | g | ISO 7765-1/A |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 25 µm, Blown Film | 0.23 | N | |
| TD : 25 µm, Blown Film | 2.7 | N | |
| Spencer Impact - Blown Film (25.0 µm) | 35.0 | MPa | ASTM D3420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxidation Induction Time (200°C) | 70 | min | EN 728 |
| Vicat Softening Temperature | 125 | °C | ISO 306/A120 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 200 to 220 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong Aobang TPU-Polyester 64-D | Shandong Aobang Chemical Technology Co.,Ltd. | TPU-Polyester | Shandong Aobang TPU-Polyester |
| MonoSol® M8440 | MonoSol, LLC | PVOH | MonoSol® |
| Unichem 7342 | Colorite Polymers | PVC, Unspecified | Unichem |
| Elastocon® 8068L | Elastocon TPE Technologies | TPE | Elastocon® |
| POCAN® A 3131 000000 | LANXESS Corporation | PBT+ASA | POCAN® |