AZDEL™ R401-B01
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Azdel, Inc. |
| Trademark: | AZDEL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1HYXLM_AZDEL-R401-B01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| AZDEL R401-B01 is a glass mat thermoplastic laminate based upon random oriented continuous fiber mat contained within polypropylene resin matrix. This composite material features high flow properties and a very homogeneous fiber distribution. This material is typically used for standard semi-structural applications and where high impact and stiffness are desired. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.10 - 0.30 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6160 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 108 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2 |
| Flexural Modulus | 6150 | MPa | ISO 178 |
| Flexural Stress | 160 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Instrumented Dart Impact | ASTM D3763 | ||
| 4.00 mm, Energy at Peak Load | 15.0 | J | ASTM D3763 |
| 4.00 mm, Total Energy | 28.1 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 154 | °C | ASTM D648 |
| CLTE - Flow (-40 to 121°C) | 4.3E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 2.8 | mm/min | ISO 3795 |
| Additional Information |
|---|
| Basis Weight, Internal Test Method: 0.9 lbs/ft²Filler Content by Weight(ashing), Internal Test Method: 40 %Multi-axial Impact Peak Force, ASTM D3763, 4mm: 845 lbsNotched Izod Impact, ISO 180, 23°C, 4mm: 810 J/mPoissons Ratio, ISO 527: 0.361Sheet Thickness, Internal Test Method: 145 milsSpecific Gravity, ASTM D792, Laminated: 1.19Specific Gravity, ASTM D792, Molded: 1.21 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® AW13BK6265 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| UNISOFT TPE™ ST-60A-BK-4-02 | UNITED SOFT PLASTICS, Inc. | SEBS | UNISOFT TPE™ |
| 4MID® 25B20400 | 4Plas | Nylon 6 | 4MID® |
| Borealis PP RA130E-1498 | Borealis AG | PP Random Copolymer | Borealis PP |
| Huafon JF-P-8060 / JF-I-6008 (Wood-like sole) | Huafon Group Co., Ltd. | PUR-Ester | Huafon |