INNOPOL® PP CS 1-3000 DEL
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Inno-Comp Ltd. |
| Trademark: | INNOPOL® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1GBV8k_INNOPOL-PP-CS-1-3000-DEL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
INNOPOL® CS 1-3000 DEL is a polypropylene homopolymer based compound. This grade is available in nature and custom coloured form as well. Recommended application INNOPOL® CS 1-3000 DEL is developed for producing injection moulded automotive products. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.920 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.0 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 10.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.96 | % | ISO 294-4 |
| Flow direction | 1.2 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1450 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 36.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 8.0 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break | 14 | % | ISO 527-2 |
| Flexural Modulus 1 | 2600 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 1.2 | kJ/m² | ISO 179/1eA |
| 23°C | 3.7 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 17 | kJ/m² | ISO 179/1eU |
| 23°C | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 101 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 54.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 153 | °C | ISO 306/A120 |
| -- | 94.0 | °C | ISO 306/B120 |
| Melting Temperature | 162 | °C | ISO 11357-3 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | FMVSS 302 | |
| flammability- Automotive materials (thickness d > 1 mm) | + | FMVSS 302 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 190 - 230 | °C | |
| Middle Temperature | 190 - 230 | °C | |
| Front Temperature | 190 - 230 | °C | |
| Processing (Melt) Temp | 210 - 240 | °C | |
| Mold Temperature | 10.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Hold pressure: 50 to 100 % of actual injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NORYL™ NH7010HF resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |
| NOVALAC FM 1132P | Vyncolit N.V. | Phenolic | NOVALAC |
| Generic Perfluoroelastomer | Generic | Perfluoroelastomer | Generic |
| Hanwha Total PP GB72 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| Hostacom TRC 333N D72645 | LyondellBasell Industries | PP Copolymer | Hostacom |