CELEX™ 5200HF.K
| Category: | PC+ABS , Polycarbonate Resin |
| Manufacturer: | Trinseo |
| Trademark: | CELEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1DnPsw_CELEX-5200HF-K.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CELEX 5200HF.K is a non-halogen ignition resistant PC/ABS alloy. It combines the superior physical properties of PC and the excellent processability of ABS. Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 18 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (3.20 mm, Injection Molded) | 2450 | MPa | ASTM D638 |
| Tensile Strength (Yield, 3.20 mm, Injection Molded) | 55.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 3.20 mm, Injection Molded) | 100 | % | ASTM D638 |
| Flexural Modulus (3.20 mm, Injection Molded) | 2600 | MPa | ASTM D790 |
| Flexural Strength (3.20 mm, Injection Molded) | 88.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C, 3.20 mm, Injection Molded | 220 | J/m | |
| 23°C, 3.20 mm, Injection Molded | 750 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 76.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 100 | °C | ASTM D1525 1 |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI Str | 60.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+11 | ohms·cm | ASTM D257 |
| Dielectric Strength | 26 | kV/mm | ASTM D149 |
| Comparative Tracking Index | > 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 2 | UL 94 | ||
| 1.40 mm | V-0 | ||
| 1.50 mm | 5VB | ||
| Glow Wire Flammability Index (1.50 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.50 mm) | 750 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 190 to 220 | °C | |
| Middle Temperature | 200 to 225 | °C | |
| Front Temperature | 205 to 235 | °C | |
| Nozzle Temperature | 210 to 235 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h), Loading 1 (10 N) |
| 2 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Styrolution PS 1611 | INEOS Styrolution Group GmbH | PS (GPPS) | Styrolution PS |
| TEREZ PA 6.6 HT 7500 GF 40 | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| Zetpol® 2020 | Zeon Corporation | NBR | Zetpol® |
| Colorite Rigid PVC 2600 UVLCR | Colorite Polymers | PVC, Rigid | Colorite Rigid PVC |
| Eltex® MED 100-MG03 | INEOS Olefins & Polymers Europe | PP Homopolymer | Eltex® MED |