Tisarbon® PC UNR
| Category: | PC , Polycarbonate |
| Manufacturer: | Tisan |
| Trademark: | Tisarbon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1CnX8e_Tisarbon-PC-UNR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Tisarbon® PC UNR is a Polycarbonate (PC) material. It is available in Africa & Middle East or Europe for injection molding. Primary attribute of Tisarbon® PC UNR: Flame Rated. |
| General Information | |
|---|---|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 22 | g/10 min | ISO 1133 |
| Molding Shrinkage | < 1.0 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | < 0.50 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 91 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 65.0 | MPa | |
| Break | 60.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 9.0 | % | |
| Break | 12 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 45 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 145 | °C | ISO 75-2/Be |
| Vicat Softening Temperature | 150 | °C | ISO 306/B120 |
| Melting Temperature | 230 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (3.00 mm) | 400 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-2 | UL 94 | |
| Glow Wire Flammability Index (3.00 mm) | 750 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 120 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Rear Temperature | 280 to 290 | °C | |
| Middle Temperature | 270 to 280 | °C | |
| Front Temperature | 260 to 270 | °C | |
| Nozzle Temperature | 280 to 290 | °C | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravago Compounds HMP-305 (Roto) | Ravago Manufacturing Americas, LLC | MDPE | Ravago Compounds |
| Vikalloy IM62 | Viking Polymers, LLC | PMMA+PVC | Vikalloy |
| NILENE® E10 K20T | Taro Plast S.p.A. | PP Copolymer | NILENE® |
| Sumiliteresin® PR-51530B | SBHPP | Phenolic | Sumiliteresin® |
| ULTEM™ 2312EPR resin | SABIC Innovative Plastics | PEI | ULTEM™ |