VERTON* UX03320 is a compound based on Polyphthalamide resin containing Long Glass. Also known as: LNP* VERTON* Compound PDX-U-03320 Product Reorder name: UX03320 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.63 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.050 - 0.10 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.080 - 0.20 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.15 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.060 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.20 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.30 | % | ISO 62 |
| Spiral flow length | Internal method | ||
| 1.00 mm | 30.0 | Internal method | |
| 3.00 mm | 70.0 | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 18200 | MPa | ASTM D638 |
| -- | 20300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture | 220 | MPa | ASTM D638 |
| Fracture | 200 | MPa | ISO 527-2 |
| Tensile Elongation (Break) | 1.9 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 18000 | MPa | ASTM D790 |
| -- 2 | 17700 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 300 | MPa | ASTM D790 |
| -- | 360 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 300 | J/m | ASTM D256 |
| 23°C 3 | 38 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 800 | J/m | ASTM D4812 |
| 23°C 4 | 70 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 15.0 | J | ASTM D3763 |
| -- | 19.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 260 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 275 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 1.2E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 2.2E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.800 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 316 - 327 | °C | |
| Middle Temperature | 321 - 332 | °C | |
| Front Temperature | 332 - 343 | °C | |
| Processing (Melt) Temp | 316 - 332 | °C | |
| Mold Temperature | 138 - 166 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RIALFLAME POLYPROPYLENE 10% TALC V2 | RIALTI Srl | PP Homopolymer | RIALFLAME |
| RTP 805 TFE 15 UV | RTP Company | Acetal (POM) Copolymer | RTP |
| Statimax 810 | Polymics, Ltd. | PBI | Statimax |
| VeroBlue™ RGD840 | Stratasys | Unspecified | VeroBlue™ |
| Flontech® FT-EK10-3 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |