ISPLEN® PP 040 N1E

Category:	PP Homopolymer , Polypropylene Homopolymer
Manufacturer:	REPSOL
Trademark:	ISPLEN®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	1BTun5_ISPLEN-PP-040-N1E.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Isplen® PP 040 N1E is a medium melt flow rate polypropylene homopolymer specially formulated and adapted for extrusion processes and particularly in thermoforming applications. It is nucleated so that it exhibits high stiffness, good transparency and excellent high temperature properties. It is recommended in sterilisation and hot filling. TYPICAL APPLICATIONS In extrusion processes such as: Mainly in sheet extrusion and thermoforming. Others are monofilament and weaving tapes. Recommended melt temperature range from 190 to 250°C. Processing conditions should be optimised for each production line.

Message

Isplen® PP 040 N1E is a medium melt flow rate polypropylene homopolymer specially formulated and adapted for extrusion processes and particularly in thermoforming applications.
It is nucleated so that it exhibits high stiffness, good transparency and excellent high temperature properties. It is recommended in sterilisation and hot filling.

TYPICAL APPLICATIONS
In extrusion processes such as:

Mainly in sheet extrusion and thermoforming.

Others are monofilament and weaving tapes.

Recommended melt temperature range from 190 to 250°C. Processing conditions should be optimised for each production line.

General Information
Features	Food Contact Acceptable Good Sterilizability High Clarity High Heat Resistance High Stiffness Medium Flow
Uses	Monofilaments Sheet Tape
Agency Ratings	EU Food Contact, Unspecified Rating
Processing Method	Extrusion Filament Extrusion Sheet Extrusion Thermoforming

Physical	Nominal Value	Unit	Test Method
Density	0.905	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	3.0	g/10 min	ISO 1133

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress (Yield)	35.0	MPa	ISO 527-2
Flexural Modulus	1600	MPa	ISO 178

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (0.45 MPa, Unannealed)	90.0	°C	ISO 75-2/B
Vicat Softening Temperature	153	°C	ISO 306/A

Extrusion	Nominal Value	Unit
Melt Temperature	190 to 250	°C

Resin Grade	Manufacturer	Category	Trademark
SABIC® PPcompound 7690	Saudi Basic Industries Corporation (SABIC)	PP, Unspecified	SABIC® PPcompound
Exact™ 3131	ExxonMobil Chemical	Plastomer	Exact™
INEOS PP 102-XA06	INEOS Olefins & Polymers Europe	PP Homopolymer	INEOS PP
Karina CLEAR PVC COMPOUND 80/208-IS-RG	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
OTECH PVC PL1001-3 - Plenum Insulation	OTECH Corporation	PVC, Unspecified	OTECH PVC