SABIC® LDPE 2801H0W
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1APR1h_SABIC-LDPE-2801H0W.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® LDPE 2801H0W offers high production output with very good optical properties, as well as good stiffness toughness balance. Application SABIC® LDPE 2801H0W is typically used for high clarity collation shrink films, glossy automatic packaging printed films and deep freeze films. SABIC® LDPE 2801H0W can typically be used for food applications due to very low migration levels. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.928 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.55 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Blown Film) | 1.0 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| MD : 30 µm, blown film | 290 | MPa | ISO 527-3 |
| TD : 30 µm, blown film | 340 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 30 µm, blown film | 13.0 | MPa | ISO 527-3 |
| TD : Yield, 30 µm, blown film | 14.0 | MPa | ISO 527-3 |
| MD : Broken, 30 µm, blown film | 21.0 | MPa | ISO 527-3 |
| TD : Broken, 30 µm, blown film | 22.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 30 µm, blown film | > 200 | % | ISO 527-3 |
| TD : Broken, 30 µm, blown film | > 500 | % | ISO 527-3 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Strength - Blown FIlm (30.0 µm) | 250 | J/cm | ASTM D4272 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Blocking - Blown Film (30.0 µm) | 10 | g | Internal method |
| Re-blocking - Blown Film (30.0 µm) | 30 | g | Internal method |
| Tear Strength 1 | ISO 6383-2 | ||
| MD : 30.0 µm | 45.0 | kN/m | ISO 6383-2 |
| TD : 30.0 µm | 35.0 | kN/m | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 106 | °C | ISO 306/A |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 30.0 µm, Blown Film) | 70 | ASTM D2457 | |
| Haze (30.0 µm, Blown Film) | 6.0 | % | ASTM D1003A |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film properties have been measured at 30 µm film with a BUR of 3. |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen HP2981 | LyondellBasell Industries | PP Homopolymer | Moplen |
| Westlake LDPE EM812AA | Westlake Chemical Corporation | LDPE | Westlake LDPE |
| NEFTEKHIM PE 5117N (18601) | Nizhnekamskneftekhim Inc. | LLDPE | NEFTEKHIM PE |
| ColorRx® PC-1500NB | LTL Color Compounders, Inc. | PC | ColorRx® |
| KOCETAL® K300HRD | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |