InnoTuf® TP-4050
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | InnoTuf® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1A7sAx_InnoTuf-TP-4050.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TP-4050 is a rigid, impact resistant polyurethane formulated for hand-batch processing, vacuum assist casting or meter mix dispense methods. Excellent physical properties can be obtained with a mild post cure without the utilization of mercury, MOCA, or TDI. TP-4050 is a tough ABS simulated product with a very low mixed viscosity and great demold characteristics. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Cured | 1.09 | g/cm³ | |
| Hardener | 1.09 | g/cm³ | |
| Base Resin | 1.21 | g/cm³ | |
| Molding Shrinkage - Flow | 0.10 to 0.50 | % | ASTM D2566 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 1550 | MPa | ASTM D790 |
| Flexural Strength | 79.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 70.0 | °C | ASTM D648 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 100 Mix Ratio by Weight: 100 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 90 | ||
| Demold Time | 45 to 75 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 38°C 1 | 0.075 | Pa·s | |
| 38°C 2 | 0.33 | Pa·s | |
| 38°C 3 | 1.1 | Pa·s | |
| Curing Time 4 | 26 | hr | |
| Gel Time | 4.0 to 6.0 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 75 to 85 | ASTM D2240 | |
| Tensile Strength | 56.5 | MPa | ASTM D638 |
| Tensile Elongation at Break | 20 | % | ASTM D638 |
| Note Message | |
|---|---|
| 1 . | Resin |
| 2 . | Mixed |
| 3 . | Hardener |
| 4 . | 2 hours at 150°F + 24 hours at 77°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Huafon JF-P-9655NA / JF-I-9622 | Huafon Group Co., Ltd. | PUR-Ester | Huafon |
| Huafon JF-P-4170T / JF-I-4118 (midsole) | Huafon Group Co., Ltd. | PUR-Ester | Huafon |
| Hylon® N2033THL | Ravago Manufacturing Americas, LLC | Nylon 6 | Hylon® |
| LNP™ STAT-LOY™ M3000C compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ STAT-LOY™ |
| Sylvin 8200-75FUV Clear 8437 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |