DOW™ Electrical & Telecommunications DGDK-6924 NT EXP1
| Category: | HDPE , High Density Polyethylene Cellular Insulation Compound |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ Electrical & Telecommunications |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 19pikb_DOWElectricalampTelecommunicationsDGDK6924NTEXP1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DGDK-6924 NT EXP1 is a high density polyethylene compound designed for use in physical foaming processes where high expansion rates (40 - 70%) are required. This compound is designed to offer excellent high speed processability as given by low extrusion pressures and smooth insulation surface quality. Furthermore, since it is fully pre-compounded with all the necessary ingredients, DGDK-6924 NT EXP1 offers better dispersion of the nucleating agent allowing high expansion rates to be achieved with more consistent processability (capacitance and diameter). It is stabilized for long term cable performance in data cable applications. Applications: Typical applications include LAN and data center cables. Specifications DGDK-6924 NT EXP1 should meet the following material specifications: - ASTM D 1248 Class A, Type III, Category 3 - ISO 1875-PE, KGHN, 45-D-045 |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 0.952 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (140°C/5.0 kg) | 5.5 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness 2(Shore D, 1 sec) | 65 | ISO 868 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxidation Induction Time (200°C) | > 50 | min | ASTM D3895 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dielectric Constant 3(1 MHz) | 2.30 | IEC 60250 | |
| Dissipation Factor (50 Hz) | 1.0E-4 | IEC 60250 |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 4 | 21.0 | MPa | IEC 60811-501 |
| Tensile Elongation at Break 5 | 1400 | % | IEC 60811-501 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 170 - 190 | °C |
| Extrusion instructions |
|---|
| DGDK- 6924 NT EXP1 can be processed using a range of commercial gas injection systems.It is normally extruded with a target melt temperature of 170 - 190 °C.Typical barrel temperatures required depend on extruder size and construction being made but a good starting point is: Feed zone: 150 - 160 °C Transition zone: 160 - 170 °C Injection Point: 185 - 200 °C Metering zone: 180 - 190 °C Cross head and Die: 200 - 210 °C |
| Note Message | |
|---|---|
| 1 . | On unannealed material from the melt flow rate extrudate |
| 2 . | Measured on compression moulded plaques |
| 3 . | Measured on compression moulded plaques |
| 4 . | Measured on extruded tape |
| 5 . | Measured on extruded tape |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Network Polymers SAN 250 | Network Polymers, Inc. | SAN | Network Polymers SAN |
| EnCom PC 1414 | EnCom, Inc. | PC | EnCom |
| KF 2950 | Kureha Corporation | PVDF | KF |
| LUBEMID B27 NATURAL UV | LUBEN PLAST srl | Nylon 6 | LUBEMID |
| OTECH ALLOY NT7000-80 - Profile | OTECH Corporation | TP, Unspecified | OTECH ALLOY |