Tenac™ 4012
| Category: | Acetal (POM) Homopolymer , Acetal (POM) Homopolymer |
| Manufacturer: | Asahi Kasei Chemicals Corporation |
| Trademark: | Tenac™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 18y42n_Tenac-4012.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Tenac™ 4012 is an Acetal (POM) Homopolymer product. It is available in Africa & Middle East, Asia Pacific, Europe, or North America. Applications of Tenac™ 4012 include engineering/industrial parts and housings. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 10 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 1.8 to 2.2 | % | Internal Method |
| Water Absorption (23°C, 24 hr, 50% RH) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 85 | ||
| R-Scale | 120 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2700 | MPa | ISO 527-2 |
| Tensile Stress | |||
| Yield | 66.0 | MPa | ISO 527-2 |
| -- | 64.0 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Break | 45 | % | ASTM D638 |
| Break | 40 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2600 | MPa | ASTM D790 |
| -- | 2500 | MPa | ISO 178 |
| Flexural Strength | 92.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 10 | kJ/m² | ISO 179 |
| Notched Izod Impact | 92 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 172 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 151 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 130 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 80.0 | °C | ISO 75-2/A |
| CLTE - Flow | 1.0E-4 | cm/cm/°C | ASTM D696, ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.840 mm | HB | ||
| 1.50 mm | HB |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V973 NAT601UV AF | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| DJSilicone NE-- T-1/NE-T-1U | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| FERROPAK® TPP40WA07BK | Ferro Corporation | PP, Unspecified | FERROPAK® |
| LUVOCOM® 1-8562 | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| Infino AE-2150 | LOTTE ADVANCED MATERIALS CO., LTD. | PC+PET | Infino |