EMAC® SP2261
| Category: | EMA , Ethylene Methyl Acrylate Copolymer |
| Manufacturer: | Westlake Chemical Corporation |
| Trademark: | EMAC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 18sQGp_EMAC-SP2261.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EMAC resins adhere to and are compatible with a wide range of materials including paper, polyolefins, oriented polyolefins, polyesters, ionomers, PVdC, unplasticized PVC and other polar polymers. For use as heat seal layer, adhesive layer, or modifier for cost/performance enhancement. They are soft, pliable and tough at ambient and freezing temperatures and exhibit excellent ESCR. These polymers exhibit high solids fillability and compatibility with a wide range of polymers. This facilitates their uses as bases for all-purpose concentrates for addition to a wide spectrum of polymers. They process like LDPE. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.950 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.5 | g/10 min | ASTM D1238 |
| Methyl Acrylate Content | 23.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 37 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 9.00 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 800 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 38 µm, Blown Film | 42.0 | MPa | |
| 1% Secant, TD : 38 µm, Blown Film | 31.0 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 38 µm, Blown Film | 19.0 | MPa | |
| TD : Break, 38 µm, Blown Film | 16.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 38 µm, Blown Film | 410 | % | |
| TD : Break, 38 µm, Blown Film | 760 | % | |
| Dart Drop Impact (38 µm, Blown Film) | 390 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm, Blown Film | 85 | g | |
| TD : 38 µm, Blown Film | 390 | g |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -73.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 45.0 | °C | ASTM D1525 |
| Peak Melting Temperature | 74.0 | °C | ASTM D3418 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 38.1 µm, Blown Film) | 23 | ASTM D2457 | |
| Haze (38.1 µm, Blown Film) | 30 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Type IV, 500 mm/min |
| 2 . | Type IV, 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Borealis PP BC612WG | Borealis AG | PP Copolymer | Borealis PP |
| ColorRx® TPV-70A0RX | LTL Color Compounders, Inc. | TPV Alloy | ColorRx® |
| LNP™ LUBRICOMP™ DX07404H compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |
| Sylvin 2900-60 White 1517 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 86052-80 Clear 8492 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |