AKROMID® B3 2 RM-D natural (3293)
| Category: | Nylon 6+ABS , Polyamide 6 + ABS |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 18oI6X_AKROMID-B3-2-RM-D-natural-3293-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® B3 2 RM-D natural (3293) is a nonreinforced, UV-stabilised polyamide 6 with limited moisture absorption and light inherent colour Applications are interior and exterior parts with very high impact strength in the automotive industry |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.07 | -- | g/cm³ | ISO 1183 |
| Spiral Flow | 55.0 | -- | cm | Internal Method |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.1 | -- | % | |
| Flow | 0.90 | -- | % | |
| Humidity Absorption - 62% RH (70°C) | 1.6 | -- | % | ISO 1110 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2000 | 1100 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 47.0 | 30.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | > 50 | > 100 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2100 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 70.0 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 15 | 17 | kJ/m² | |
| 23°C | 70 | 85 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 100 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 67.0 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 112 | -- | °C | ISO 306/B50 |
| Melting Temperature 3 | 225 | -- | °C | DIN EN 11357-1 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 4(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10 K/min, DSC |
| 4 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Monprene® CP-13057G CLR | Teknor Apex Company | TPE | Monprene® |
| NEFTEKHIM PS 430M | Nizhnekamskneftekhim Inc. | PS (GPPS) | NEFTEKHIM PS |
| Chiao Fu PA66/6 MB312GM45 BK | Chiao Fu Enterprises Co., Ltd. | Nylon 66/6 | Chiao Fu PA66/6 |
| DJSilicone NE-G140 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| Elastollan® 688A10N | BASF Corp. Thermoplastic Polyurethanes | TPU-Polyester | Elastollan® |