SABIC® PPcompound 6614
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 18ZTGd_SABIC-PPcompound-6614.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PPcompound 6614 is a mineral filled modified polypropylene. This material combines high flow, good impact and a high stiffness level with a low shrinkage and CLTE. Typical applications include automotive exterior parts such as large thin wall zero gap bumper designs but also lateral siding and bumper strips. It can be used in painted and unpainted applications with UV stabilization added on demand. SABIC® PPcompound 6614 is a designated automotive grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.00 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 20 | g/10 min | ISO 1133 |
| Molding Shrinkage (24 hr) | 0.75 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Injection Molded) | 60 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/5/50 | ||
| Yield, 3.20 mm, Injection Molded | 19.0 | MPa | |
| Break, 3.20 mm, Injection Molded | 18.0 | MPa | |
| Tensile Strain (Break, 3.20 mm, Injection Molded) | 500 | % | ISO 527-2/5/50 |
| Flexural Modulus 1(Injection Molded) | 1350 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | 35 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (-40°C, Injection Molded) | 40 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | ISO 180/4A | ||
| -20°C, Injection Molded | 10 | kJ/m² | |
| 0°C, Injection Molded | No Break | ||
| 23°C, Injection Molded | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 100 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 130 | °C | ISO 306/A |
| CLTE - Flow | ASTM D696 | ||
| -30 to 30°C | 5.5E-5 | cm/cm/°C | |
| 23 to 80°C | 8.5E-5 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | Method I (3 point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4765 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| SCANAMID 66 A12^ F25 FR6 | Polykemi AB | Nylon 66 | SCANAMID 66 |
| Andur 70 DP | Anderson Development Company | PUR-Ether/TDI | Andur |
| Emulprene® 1012 | INSA | SBR, Emulsion | Emulprene® |
| LNP™ LUBRICOMP™ KL004A compound | SABIC Innovative Plastics | Acetal (POM) Homopolymer | LNP™ LUBRICOMP™ |