Order Products : sales@su-jiao.com
POLYabs F20 GF17
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Polykemi AB |
| Trademark: | POLYabs |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 17QfnH_POLYabs-F20-GF17.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass fibre reinforced |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.16 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 10 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.25 to 0.45 | % | |
| Flow | 0.25 to 0.45 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 42.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 4700 | MPa | ISO 178 |
| Flexural Stress | 75.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1 | |||
| 0.45 MPa, Unannealed | 105 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 95.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 105 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECOLITE KM-747(J) | KYOCERA Chemical Corporation | Phenolic | TECOLITE |
| VENELENE® 2706 | Poliolefinas Internacionales, C.A. (Polinter) | LLDPE | VENELENE® |
| KW Plastics KW 621-T20 | KW Plastics | PP Impact Copolymer | KW Plastics |
| Sylvin 3280-80 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| SQUARE® SSR2026-50A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone | SQUARE® |