Arylmax® K6020GF30
| Category: | PAEK , Polyaryletherketone |
| Manufacturer: | Polymics, Ltd. |
| Trademark: | Arylmax® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 16PZds_Arylmax-K6020GF30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyaryletherketone, 30% Glass Fiber Filler |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 | g/cm³ | ASTM D792 |
| Water Absorption (23°C, 24 hr) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11700 | MPa | ASTM D638 |
| Tensile Strength | 170 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.6 | % | ASTM D638 |
| Flexural Modulus | 11700 | MPa | ASTM D790 |
| Flexural Strength | 240 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 168 | °C | ASTM D3418 |
| Melting Temperature | 330 | °C | DSC |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 180 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 380 | °C | |
| Middle Temperature | 380 | °C | |
| Front Temperature | 380 | °C | |
| Nozzle Temperature | 380 | °C | |
| Mold Temperature | 200 to 210 | °C | |
| Injection Rate | Fast | ||
| Screw Compression Ratio | 2.5:1.0 to 3.5:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radiflam® A RV300 HF 339 NER | Radici Plastics | Nylon 66 | Radiflam® |
| S&E General Purpose G-94-142A | S&E Specialty Polymers, LLC | PVC, Flexible | S&E General Purpose |
| SIMONA® PP-DWU AlphaPlus® | SIMONA AMERICA, Inc. | PP, Unspecified | SIMONA® |
| Spartech Polycom PP6850R B38 | Spartech Polycom | PP, Unspecified | Spartech |
| Sunny® PA66 EB130 | Guangdong Shunde Shunyan New Material Co., Ltd. | Nylon 66 | Sunny® |