SMOKEGUARD™ III 1041 NATURAL B
| Category: | PVC, Unspecified , Polyvinyl Chloride |
| Manufacturer: | AlphaGary |
| Trademark: | SMOKEGUARD™ III |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 15sEEc_SMOKEGUARD-III-1041-NATURAL-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A LEAD FREE, 75°C RATED, FLAME RETARDED COMPOUND INTENDED FOR PLENUM INSULATION APPLICATIONS. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.58 - 1.62 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw D | 67 - 73 | ASTM D2240 | |
| Shaw D, 15 seconds | 54 - 60 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D412 | ||
| 0.381 mm | 16.5 | MPa | ASTM D412 |
| 1.91 mm | 14.5 | MPa | ASTM D412 |
| Tensile Elongation | ASTM D412 | ||
| Fracture, 1.91mm | 200 | % | ASTM D412 |
| Fracture, 0.381mm | 180 | % | ASTM D412 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -5.00 | °C | ASTM D746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index (3.18 mm) | 50 | % | ASTM D2863 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 154 | °C | |
| Cylinder Zone 2 Temp. | 166 | °C | |
| Cylinder Zone 3 Temp. | 171 | °C | |
| Cylinder Zone 4 Temp. | 177 | °C | |
| Cylinder Zone 5 Temp. | 177 | °C | |
| Adapter Temperature | 177 | °C | |
| Melt Temperature | 182 - 188 | °C | |
| Die Temperature | 177 | °C | |
| Extruder Screw Compression Ratio | 3.0:1.0 |
| Extrusion instructions |
|---|
| Melt temperatures is critical, at excessive temperatures foaming may occur. It may be necessary to adjust barrel temp to attain the desired melt temperature. Material should be dried prior to use |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| APEX® 80853-A | Teknor Apex Company | PVC, Flexible | APEX® |
| Formolene® L62009H | Formosa Plastics Corporation, U.S.A. | LLDPE | Formolene® |
| Karina WHITE PVC COMPOUND 70900-10/25-E-IS-LMP (226467) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| StarFlex® 7092-1003 | Star Thermoplastic Alloys & Rubbers, Inc. | TPE | StarFlex® |
| Sylvin 86038-60UV Clear 876 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |