LNP™ VERTON™ MV00ASU compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ VERTON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 151U1D_LNPVERTONMV00ASUcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP VERTON* MV00ASU is a compound based on Polypropylene resin containing Long Glass. Added features of this material include: Chemically Coupled. Also known as: LNP* VERTON* Compound MFX-700-10 HS UV Product reorder name: MV00ASU |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.35 | g/cm³ | ASTM D792 |
| -- | 1.33 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 10400 | MPa | ASTM D638 |
| -- | 13900 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture | 131 | MPa | ASTM D638 |
| Fracture | 141 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 1.9 | % | ASTM D638 |
| Fracture | 1.7 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 9340 | MPa | ASTM D790 |
| -- | 11100 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 187 | MPa | ASTM D790 |
| -- | 214 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 210 | J/m | ASTM D256 |
| 23°C 2 | 29 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 66 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 13.0 | J | ASTM D3763 |
| -- | 13.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, unannealed, 64.0mm span 4 | 134 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 157 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 160 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 3.4E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 4.6E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 232 - 243 | °C | |
| Middle Temperature | 243 - 254 | °C | |
| Front Temperature | 249 - 260 | °C | |
| Processing (Melt) Temp | 221 - 249 | °C | |
| Mold Temperature | 37.8 - 65.6 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PC GN1003FL | Sincerity Australia Pty Ltd. | PC | Sindustris PC |
| Softflex® 0954 | Network Polymers, Inc. | TPE | Softflex® |
| Toyolac® 824V X01 | Toray Plastics (Malaysia) Sdn. Bhd. | ABS | Toyolac® |
| Fiberfil® PP-60/TC/40/OP WT2595 | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| Plaslube® PP GF30 TL15 | Techmer Engineered Solutions | PP, Unspecified | Plaslube® |