ALCUDIA® LDPE CP-121
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | REPSOL |
| Trademark: | ALCUDIA® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 13bvil_ALCUDIALDPECP121.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ALCUDIA® CP-121 is high molecular weight, low density polyethylene compound designed for telephone and coaxial cables. This product provides a superior performance at high-speed extrusion together with a smooth surface finish of the cable. This grade contains a special stabilization system for protection against thermal and shear degradation during processing and it also contains a metal deactivator to ensure long-term ageing properties. TYPICAL APPLICATIONS Solid insulation for telephone cables It is recommended a temperature profile between 150 - 220°C. Optimal processing conditions must be tuned for each production line, recommending to use filters and a break plate to increase the pressure in the cylinder and consequently improve the cable quality, homogenization and dispersion of pigments in the case of colored cable ALCUDIA® CP-121 meets the following specifications: ISO 1872 PE KHN 23D003; ASTM D 1248 I, A5, Grade E5; NF C 32-060 ISM1; VDE 0207 Teil 2 24I1. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.921 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.35 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 16.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 600 | % | ISO 527-2 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Retention of Mechanical Properties 1(100°C) | > 70 | % | ISO 527-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset 2(200°C) | % | IEC 60811-2-1 | |
| Oxidation Induction Time (200°C) | > 30 | min | EN 728 |
| Brittleness Temperature 3 | -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 96.0 | °C | ISO 306/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | > 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Constant (1 MHz) | 2.30 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 3.0E-4 | ASTM D150 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 150 - 220 | °C |
| Note Message | |
|---|---|
| 1 . | 10 days |
| 2 . | 20 N/cm², 1.9% Peroxide + 0.2% AO |
| 3 . | 0 Failures |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® STAMAX 40YM240E | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® STAMAX |
| ACCUTECH™ CP0436W10L | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| Appeel® 45D747 | DuPont Packaging & Industrial Polymers | Polyolefin, Unspecified | Appeel® |
| Daelim Po1y® LH860 | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| Iupilon® S-2000 | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |