| PPS, cross-linked, 40% glass fiber reinforced |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.65 | g/cm³ | ISO 1183 |
| Water Absorption (Saturation, 23°C) | 0.020 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 14500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 190 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.8 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 40 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 270 | °C | ISO 75-2/A |
| Melting Temperature 1 | 285 | °C | ISO 11357-3 |
| CLTE - Flow | 2.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flammability Classification 2(0.800 mm) | V-0 | IEC 60695-11-10, -20 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | UL Registered |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYshine PBT D223 GF10 FR | Polykemi AB | PBT | POLYshine |
| Mytex® AS33L(W)-06 | Mytex Polymers | PP, Unspecified | Mytex® |
| Iupilon® GPN2030DF | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| Petrothene® LP500210 | LyondellBasell Industries | HDPE | Petrothene® |
| Polyclear® Splash PET 3301 | Indorama Ventures Polymers México | PET | Polyclear® |