Ferro PP VX-34035
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Ferro Corporation |
| Trademark: | Ferro PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 12kAUA_Ferro-PP-VX-34035.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ferro PP VX-34035 is a polypropylene copolymer (PP Copoly) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. The typical application field of Ferro PP VX-34035 is: automotive industry |
| General Information | |
|---|---|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.898 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 37 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.6 | % | ASTM D955 |
| Transverse flow | 1.7 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 73 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 21.0 | MPa | ASTM D638 |
| Flexural Modulus (102mm span) | 1310 | MPa | ASTM D790 |
| Flexural Strength (102mm span) | 33.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 53 | J/m | ASTM D256 |
| 23°C | 96 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.50mm | 143 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.50mm | 88.0 | °C | ASTM D648 |
| CLTE - Flow (-30 to 80°C) | 8.6E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 54 | mm/min | ISO 3795 |
| Additional Information |
|---|
| DuPont Impact, 2mm, 23°C: 27 JDuPont Impact, 2mm, -30°C: 18 JTensile Strength, % Break by Grip: 30%Burn Rate: t=2mm: 54 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8695-78 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| NYLEM® 66 GFR 40 IM | EMAS Plastik San.Tic.AS. | Nylon 66 | NYLEM® |
| ECOGRAN® PEHDE Soufflage BLK | Eurocompound Polymers | HDPE | ECOGRAN® |
| Laser+® C (C60A) | DAK Americas LLC | PET | Laser+® |
| POLYFORT® FPP 1876 | A. Schulman Inc. | PP, Unspecified | POLYFORT® |