Generic ABS+SAN
| Category: | ABS+SAN , Acrylonitrile Butadiene Styrene + SAN |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 12cFkD_Generic-ABS-SAN.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic ABS+SAN This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.08 to 1.09 | g/cm³ | ASTM D792 |
| 23°C | 1.07 to 1.08 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/3.8 kg | 5.9 to 38 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 16 to 98 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 121 to 123 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3830 to 4090 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 41.6 to 74.0 | MPa | |
| Break, 23°C | 53.6 to 74.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield, 23°C | 1.4 to 2.9 | % | |
| Break, 23°C | 1.7 to 2.9 | % | |
| Flexural Modulus | |||
| 23°C | 3440 to 3900 | MPa | ASTM D790 |
| 23°C | 3460 | MPa | ISO 178 |
| Flexural Stress | |||
| 23°C | 36.3 to 92.0 | MPa | ISO 178 |
| Yield, 23°C | 66.2 to 134 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 1.1 to 1.5 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 14 to 46 | J/m | ASTM D256 |
| 23°C | 1.6 to 3.2 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 95.2 to 110 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 82.7 to 100 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 82.9 to 99.6 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 102 to 118 | °C | ISO 306 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Akulon® F136-C | DSM Engineering Plastics | Nylon 6 | Akulon® |
| Americas Styrenics EA6740 | Americas Styrenics LLC | PS (HIPS) | Americas Styrenics |
| Fainplast PVC GK 89 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Hifax TRC 277P G14008 | LyondellBasell Industries | PP Copolymer | Hifax |
| Sylvin 9048-70 CLEAR | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |