Moplen HP425J
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | PolyMirae |
| Trademark: | Moplen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 12GAIo_MoplenHP425J.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Moplen HP425J is a modified polypropylene homopolymer containing a Calcium Stearate free stabilization package. It does not contain any slip or antiblocking additives. Moplen HP425J is designed for the high speed production of BOPP films. It is used by customers for a broad range of applications including metallizable films and both plain and coextruded structures. BOPP films produced with Moplen HP425J exhibit balanced mechanical properties, good transparency, gloss and enhanced shrinkage properties. For regulatory information please refer to Moplen HP425J Product Stewardship Bulletin (PSB). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 70 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1450 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 33.0 | MPa | ASTM D638 |
| Yield | 34.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield | 11 | % | ASTM D638 |
| Yield | 10 | % | ISO 527-2/50 |
| Fracture | 410 | % | ISO 527-2/50 |
| Flexural Modulus | 1400 | MPa | ASTM D790 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Tangent 1(20 µm) | 2400 | MPa | MA 18068 |
| Tensile Stress 2(Break, 20 µm) | 116 | MPa | MA 18068 |
| Tensile Elongation 3(Break, 20 µm) | 29 | % | MA 18068 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 330 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 93.0 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 88.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 152 | °C | ISO 306/A50 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (20.0 µm) | 0.50 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 5 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEPAZ™ VL140 | Mando Advanced Materials Co., Ltd. | PPA | SEPAZ™ |
| AKROMID® A3 GF 30 4 6 black 950058 (1369) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| ELASTOSIL® RT 604 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® RT |
| Karina IVORY PVC COMPOUND -E 707-35/ 1-D-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Delon 4040 | Shanghai Lin Gen Rubber Materials Co., Ltd. | TEEE | Delon |