LNP™ THERMOCOMP™ JF006 compound
| Category: | PESU , Polyethersulfone |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 11qZNC_LNP-THERMOCOMP-JF006-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP JF006 is a compound based on Polyethersulfone resin containing Glass Fiber. Also known as: LNP* THERMOCOMP* Compound JF-1006 Product reorder name: JF006 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.59 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (345°C/10.0 kg) | 10.0 to 20.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 0.20 to 0.40 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 142 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 8200 | MPa | ISO 178 |
| Flexural Stress | 192 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 3(23°C) | 8.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(23°C) | 40 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5(1.8 MPa, Unannealed, 64.0 mm Span) | 210 | °C | ISO 75-2/Af |
| CLTE - Flow (23 to 60°C) | 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.500 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 343 to 354 | °C | |
| Middle Temperature | 360 to 371 | °C | |
| Front Temperature | 371 to 382 | °C | |
| Processing (Melt) Temp | 354 to 371 | °C | |
| Mold Temperature | 138 to 149 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quantum Composites QC-8744FR | Quantum Composites Inc. | Vinyl Ester | Quantum Composites |
| Fainplast PVC RH 306/W | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| Eco-Solutions GP9002W | MINIMA Technoloy Co. Ltd. | Biodeg Polymers | Eco-Solutions |
| Hifax BC 72 G | LyondellBasell Industries | PP Copolymer | Hifax |
| RONFALIN® ABS 1413 GB 20 | A. Schulman Europe | ABS | RONFALIN® |