Starex TX-0520T
| Category: | MABS , Methyl Methacrylate / ABS |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Starex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0zl03f_Starex-TX-0520T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starex TX-0520T is an Acrylonitrile Butadiene Styrene (ABS) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary characteristic: flame rated. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 15 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale | 106 | ASTM D785 | |
| R-Scale | 110 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2100 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 1 | 42.0 | MPa | ASTM D638 |
| Yield | 47.0 | MPa | ISO 527-2/50 |
| Break | 34.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 15 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 2 | 2000 | MPa | ASTM D790 |
| -- 3 | 2200 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 4 | 59.0 | MPa | ASTM D790 |
| -- 5 | 70.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 6(23°C) | 12 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 160 | J/m | ASTM D256 |
| 23°C 7 | 12 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed, 4.00 mm | 81.0 | °C | ISO 75-2/B |
| 0.45 MPa, Annealed | 85.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 4.00 mm | 71.0 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed, 4.00 mm | 80.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 87.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (3200 µm) | 88.0 | % | ASTM D1003 |
| Haze (3200 µm) | 3.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 | °C | |
| Desiccant Dryer | 80.0 | °C | |
| Drying Time | |||
| -- | 4.0 to 6.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 180 to 190 | °C | |
| Middle Temperature | 200 to 210 | °C | |
| Front Temperature | 220 to 230 | °C | |
| Nozzle Temperature | 230 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C | |
| Injection Pressure | 49.0 to 196 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 2.8 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | Thickness: 4 mm |
| 7 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® A9945T | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Cheng Yu 3276 | Cheng Yu Plastic Company Limited | TPE | Cheng Yu |
| KOPA® KN133G30BLL | Kolon Plastics, Inc. | Nylon 6 | KOPA® |
| IROCOAT® CA-236 | Huntsman Corporation | TPU, Unspecified | IROCOAT® |
| LNP™ FARADEX™ AS003 compound | SABIC Innovative Plastics | ABS | LNP™ FARADEX™ |