MarFlex® 9607
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Chevron Phillips Chemical Company LLC |
| Trademark: | MarFlex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0ymq5M_MarFlex-9607.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MarFlex®9607 is a high density polyethylene material,. This product is available in North America or Latin America. The processing method is: co-extrusion molding or casting film. MarFlex®The main features of the 9607 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.962 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 6.5 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 32 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 32 µm, cast film | 758 | MPa | ASTM D882 |
| 1% secant, TD : 32 µm, cast film | 841 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 32 µm, extruded film | 29.0 | MPa | ASTM D882 |
| TD : Broken, 32 µm, extruded film | 23.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 32 µm, extruded film | 870 | % | ASTM D882 |
| TD : Broken, 32 µm, extruded film | 790 | % | ASTM D882 |
| Water Vapor Transmission Rate (32 µm, Cast Film) | 5.0 | g/m²/24 hr | ASTM F1249 |
| Dart Drop Test - Cast Film (31.8 µm) | 15.4 | kN/m | ASTM D1709 |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 31.8 µm | 13.5 | kN/m | ASTM D1922 |
| TD : 31.8 µm | 38.6 | kN/m | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°, 31.8 µm, Cast Film) | 120 | ASTM D2457 | |
| Haze (31.8 µm, Cast Film) | 11 | % | ASTM D1003 |
| Additional Information |
|---|
| Testing performed on a cast line at 500°F and a 0.025 in die gap. |
| Note Message | |
|---|---|
| 1 . | Cast Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinpolene MBB3134 | Teknor Apex Asia Pacific PTE. LTD. | PP, Unspecified | Sinpolene |
| Vydyne® R550H NT662 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| Ultralloy™ 50 | Hapco Inc. | TP, Unspecified | Ultralloy™ |
| Flexalloy® 9604-75 | Teknor Apex Company | PVC Elastomer | Flexalloy® |
| LNP™ THERMOCOMP™ RX99732C compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |