Product Description
TOPAS 6013S-04 is a general purpose injection molding grade with a 130°C heat distortion temperature. It is a glass-clear amorphous polymer with outstanding moisture barrier, chemical resistance, high purity and a non-reactive surface making it an excellent choice for healthcare and other high-tech products. Lower leachables and extractables of TOPAS COC preserve food and drug stability and quality. It is a non-polar substrate that does not promote adsorption, denaturation, aggregation, or precipitation like glass can. This grade has a high heat distortion temperature to withstand 121°C steam sterilization protocols, as well as gamma and EtO procedures.

Selected Applications

Drug delivery

Labware

Optics

Electronics

Food packaging

Healthcare and food contact

Leading Attributes

Low leachables & extractables, low water transmission

Temperature resistance, clarity and purity

Clarity, low birefringence, low moisture sensitivity

Low dielectric constant, thermoplastic

Not manufactured with BPA, phthalates, or halogens

Broad regulatory compliance

Related Grades for Injection Molding, Healthcare, Optics and Diagnostics

TOPAS 6013M-07 - broader processing version especially suited for IBM/ISBM

TOPAS 6015S-04 - higher heat distortion temperature (150°C) for 134°C protocols

TOPAS 5013L-10 - high flow grade, lubricated for greater processing versatility

TOPAS 5013S-04 - high flow grade without lubricant

TOPAS IT X1 - impact grade for applications requiring extra toughness

General Information
Features	High purity Low extract Moisture proof Radiation disinfection Copolymer Ethylene oxide disinfection Good chemical resistance Heat resistance, high Definition, high Compliance of Food Exposure General BPA-free amorphous Halogen-free Disinfect with steam
Uses	Electrical/Electronic Applications Optical applications Laboratory apparatus Food packaging General Medical/nursing supplies
Agency Ratings	DMF 12132 FDA FCN 405 ISO 10993 USP Class VI Europe 10/1/2011 12:00:00 AM
Appearance	Clear/transparent
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.02	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (260°C/2.16 kg)	13	g/10 min	ISO 1133
Melt Volume-Flow Rate (MVR) (260°C/2.16 kg)	14.0	cm³/10min	ISO 1133
Molding Shrinkage ¹	0.50 - 0.70	%	Internal method
Water Absorption (Saturation, 23°C)	0.010	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	2900	MPa	ISO 527-2/1A/1
Tensile Stress (Yield)	63.0	MPa	ISO 527-2/1A/50
Tensile Strain (Yield)	2.7	%	ISO 527-2/1A/50

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	1.8	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	15	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (0.45 MPa, Unannealed)	130	°C	ISO 75-2/B
Glass Transition Temperature	138	°C	ISO 11357-2
Vicat Softening Temperature	137	°C	ISO 306/B50

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity	> 1.0E+16	ohms·cm	IEC 60093
Relative Permittivity			IEC 60250
1 kHz	2.35		IEC 60250
10 kHz	2.35		IEC 60250
Dissipation Factor (1.00 GHz)	7.0E-5		IEC 60250
Comparative Tracking Index	> 600	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.60 mm)	HB		UL 94

Optical	Nominal Value	Unit	Test Method
Refractive Index	1.530		ISO 489
Transmittance	91.0	%	ISO 13468-2

Injection	Nominal Value	Unit
Drying Temperature	100	°C
Drying Time	4.0 - 6.0	hr
Rear Temperature	230 - 260	°C
Middle Temperature	240 - 280	°C
Front Temperature	260 - 290	°C
Nozzle Temperature	240 - 300	°C
Processing (Melt) Temp	240 - 300	°C
Mold Temperature	95.0 - 130	°C
Injection Pressure	50.0 - 110	MPa
Injection Rate	Moderate-Fast
Holding Pressure	30.0 - 60.0	MPa
Back Pressure	< 15.2	MPa
Screw Speed	50 - 200	rpm

Injection instructions
Feed temperature: <100°C (<212°F)Max. Residence Time: <15 minutes; short interruptions to cycle >10 minutes, reduce Tx = 170°C (338°F)Injection speed: 50 - 150 mm/sec (2.0 - 6.0 in/sec)Nozzle type: Free flow

Note Message
1 .	Dependent on processing conditions and part design.

Resin Grade	Manufacturer	Category	Trademark
Reslen PPH 10K	Polimarky Spolka Jawna	PP Homopolymer	Reslen
EPDM 774R	The Dow Chemical Company	EPDM	EPDM
INSTRUC PA612GF30	Infinity LTL Engineered Compounds	Nylon 6/12	INSTRUC
Lotader® AX 8900	Arkema	EMAAA	Lotader®
PETILEN F2-12	PETKIM Petrokimya Holding A.S.	LDPE	PETILEN