Strator® TA-X5
| Category: | PPA , Polyphthalamide |
| Manufacturer: | EPIC Polymers |
| Trademark: | Strator® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0xOLVN_Strator-TA-X5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| STRATOR® TA-X5 is a Polyphthalamide (PPA) product filled with long glass fiber. It is available in Europe. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.61 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.25 | -- | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.80 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ISO 527-2 | |||
| 23°C | 18700 | 18300 | MPa | |
| 90°C | 18000 | 16000 | MPa | |
| 120°C | 14800 | -- | MPa | |
| Tensile Stress | ISO 527-2 | |||
| Yield, 23°C | 295 | 280 | MPa | |
| Yield, 90°C | 270 | 220 | MPa | |
| Yield, 120°C | 200 | -- | MPa | |
| Tensile Strain (Break, 23°C) | 2.0 | 2.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 17500 | 17100 | MPa | ISO 178 |
| Flexural Stress (23°C) | 440 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 15 | -- | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 85 | -- | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 300 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 285 | -- | °C | ISO 75-2/A |
| CLTE - Flow (23°C) | 2.0E-5 | -- | cm/cm/°C | ISO 7991 |
| Thermal Conductivity | 0.35 | -- | W/m/K | ISO 22007 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | -- | ohms | ASTM D257 |
| Electric Strength | 35 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Extrusion | Dry | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 320 to 340 | °C | |
| Cylinder Zone 2 Temp. | 320 to 335 | °C | |
| Cylinder Zone 3 Temp. | 320 to 335 | °C | |
| Cylinder Zone 4 Temp. | 325 to 340 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLON IR 1500 | POLYMA Kunststoff GmbH & Co. KG | PC | POLYLON |
| RAMTOUGH PZ725 | Polyram Ram-On Industries | PC | RAMTOUGH |
| SUMIKASUPER® LCP E6808 WO2 | Sumitomo Chemical Co., Ltd. | LCP | SUMIKASUPER® LCP |
| Ateva® 1231 | Celanese EVA Performance Polymers | EVA | Ateva® |
| Karina WHITE PVC COMPOUND 850-10/116-Y-ERYB-AS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |